Stainless Steel Shot

Stainless Steel Shot

Types：0.2~2.5mm

Chemical Composition:

                    304 Austenite Type：C＜0.15%   Cr=16～18%  Ni=6～10%   Si＜1%  Mn＜2%

                    430  AusteniteType：   C＜0.15%  Cr=16～18%   Si＜1%   Mn＜1%

                    410  Austenite Type：C＜0.15%   Cr=11～13%  Si＜1%   Mn＜1% 

                   （Note: other chemical components can be provided.）

Micro Hardness：308~509HV（Vickers）

                32~50HRC  (Rockwell)

Durability： 6500 times

Microstructure：304 type: Deformed Austenite

               430type: Deformed Ferrit

               410type: Deformed Martensite

Density：   7.8g/cm3

Applications:

Rust-removing: Shot blasting rust-removal, shot peening rust-removal casting parts rust-removal, forged parts and steel plat 

rust-removal, H-beam steel rust-removal, steel structure rust-removal.

Intensifying: Shot blasting intensifying of stainless steel parts and heat treatment parts. 

Stainless steel shot peening: Shot peening of Colored aluminum, copper, magnesium die-casting and stainless steel.

Application Devices:

Stainless steel shot is kind of abrasive used for shot blasting machine, shot blasting equipment, shot peening machine, 

shot peening equipment, sandblasting machine, sandblasting equipments, steel material pretreatment production line, 

steel plate pretreatment production line, steel structure pretreatment production line.